Abstract
The article were studied the e ect of detonation spraying on the structure and properties of Al 2 O 3 coatings. It was determined that reducing the delay time between shots is leading to increase the hardness and elastic module of Al 2 O 3 coatings. It was found on the basis of X-ray di raction analysis that the main reason for the increasing in hardness with a decreasing in the delay time between shots is associated with increasing in the volume fraction of α -Al 2 O 3 phase. The studies of X-ray di raction presented that the highest content of the phase is achieved when the coatings are formed with a delay time between shots of 0.25 s. It was found that increasing in the volume fraction of the α -Al2O3 phase is caused by the secondary recrystallization γ → α , which occurs due to the heating of particles during coating formation, i.e. due to increasing in temperature above 1100 ◦ C in single spots of the coating when they are put each other.
Recommended Citation
Rakhadilov, B. K.; Buytkenov, D. B.; Kakimzhanov, D.; Kozhanova, R. S.; and Bektasova, G. S.
(2020)
"The effect of detonation spraying on the phase composition and hardness of Al2O3 coatings,"
Eurasian Journal of Physics and Functional Materials: Vol. 4:
No.
2, Article 7.
DOI: https://doi.org/10.29317/ejpfm.2020040207
First Page
160
Last Page
166
Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 International License.